Penzaelektrod welding electrodes: a universal solution for welding in any conditions!

The electrodes do not require calcination under standard storage conditions, which significantly speeds up the process, and are also resistant to moisture and minor contamination. They are suitable for novice welders and for working in the field at low currents. Available in various weight categories and diameters.

Welding electrodes OZS-12

Description of the electrodes

• If the storage conditions are met, they do not require calcination before welding.
• In case of humidification, calcination at a temperature of 140-150 ° C for 30 minutes.
• Coefficient of surfacing of OZC electrodes-12– 8,5-9,2 g/A*hour.
• The consumption of electrodes per 1 kg of deposited metal at OZS-12 is 1.69 kg.

Scope of application

OZS-12 electrodes are designed for welding any structures made of carbon and low-alloy steel. It is recommended for welding T-bar and lap joints, as it has a high penetration depth.

Additional

Package type

Box	Vacuum tube

Weight:1 kg, 1.5 kg, 1.9 kg, 5 kg

Diameter: 2.5mm, 3 mm, 4 mm, 5 mm, 6 mm

MR-3 FLAGMAN welding electrodes are green

Description of the electrodes

• If the storage conditions are met, they do not require calcination before welding.
• In case of humidification, calcination at a temperature of 90-100 °° C for 30 minutes (for ø 2.5 and 3.0 mm) and 120-130 °C for 1 hour (for ø 4.0 and 5.0 mm)
• The surfacing coefficient of the MR-3 FLAGMAN green electrodes is 8.5-9.2 g/Ah.
• The consumption of electrodes per 1 kg of deposited metal in the FLAGMAN MP-3 is 1.69 kg.

Scope of application

The MP-3 FLAGMAN green electrodes are designed for manual arc welding of any structures made of carbon and low-alloy steel. Welding can be carried out even by a novice welder on devices of the budget segment. Electrodes are indispensable for welding in "fields" with low current strength. The surface may be wet, with traces of rust and other contaminants. The MP-3 FLAGMAN green electrode melts quietly during welding, creates almost no splashes, and forms a fine-grained seam. When cooling, the slag lifts itself and the seam remains clean without additional mechanical impact.

Additional

Package type

Box	Vacuum tube

Weight: 1 kg, 1.5 kg, 1.9 kg, 2.5 kg, 5 kg

Diameter: 2 mm, 2.5mm, 3 mm, 4 mm, 5 mm, 6 mm

Welding electrodes MP-3

Description of the electrodes

• If the storage conditions are met, they do not require calcination before welding.
• In case of humidification, calcination at a temperature of 140-150 ° C for 30 minutes.
• Electrode surfacing coefficient MP-3 – 8,5-9,2 g/A*hour.
• The consumption of electrodes per 1 kg of deposited metal for MP-3 is 1.69 kg.

Scope of application

The MP-3 electrodes are designed for welding any structures made of carbon and low-alloy steel. Welding can be carried out even by a novice welder on devices of the budget segment. Electrodes are indispensable for welding in "fields" with low current strength. The surface may be wet, with traces of rust and other contaminants.

Additional

Package type

Box	Vacuum tube

Weight:1 kg, 1.5 kg, 1.9 kg, 2.5 kg, 5 kg

Diameter: 2 mm, 2.5 mm, 3 mm, 4 mm, 5 mm, 6 mm

MP-3C welding electrodes

Description of the electrodes

• If the storage conditions are met, they do not require calcination before welding.
• In case of humidification, calcination at a temperature of 140-150 ° C for 30 minutes.
• The welding coefficient of the MR-3C electrodes is 8.5-9.2 g/A*h.
• The consumption of electrodes per 1 kg of deposited metal for MP-3S is 1.69 kg.

Scope of application

The MR-3C electrodes are designed for welding any structures made of carbon and low-alloy steel. Electrodes are widely used in construction.

Additional

Package type

Box	Vacuum tube

Weight: 1 kg, 1.5 kg, 1.9 kg, 5 kg

Diameter: 2.5mm, 3 mm, 4 mm, 5 mm, 6 mm

Welding electrodes ANO-21 Standard FLAGMAN

Description of the electrodes

ANO-21 STANDARD electrodes are designed for welding any carbon steel structures according to GOST 380 (St 0, St 1, St 2, St 3) of all degrees of deoxidation- KP, PS, SP and according to GOST 1050 (05kp, 08kp, 08ps, 08, 10kp, 10ps, 10, 15kp, 15ps, 15, 20kp, 20ps, 20).

The electrodes are designed for welding angular, butt, and lap joints in all spatial positions, including vertical seams using the top-down method. Electrodes are indispensable for welding when high demands are placed on the quality of the seam.

• Made according to an improved formulation.
• Welding can be carried out even by a novice welder on devices of the budget segment.
• They are indispensable for welding root seams. Slag does not interfere with the control of the welding process
• When welding, they do not create splashes, they form a fine-scaled seam.
• When cooling, the slag lifts itself and the seam remains clean without additional mechanical impact.
• If the storage conditions are met, they do not require calcination before welding.
• In case of humidification, calcination at a temperature of 90-100 °° C for 30 minutes (for ø 2.5 and 3.0 mm) and 120-130 °C for 1 hour (for ø 4.0 and 5.0 mm)
• The coefficient of electrode deposition is 8.5–9.2 g/A*h.
• The consumption of electrodes per 1 kg of deposited metal is 1.69 kg.

Scope of application

ANO-21 Standard FLAGMAN electrodes are designed for manual arc welding of any structures made of carbon and low-alloy steel. Welding can be carried out even by a novice welder on devices of the budget segment. Electrodes are indispensable for welding in "fields" with low current strength. The surface may be wet, with traces of rust and other contaminants. The ANO-21 Standard FLAGMAN electrode melts quietly during welding, creates almost no splashes, and forms a fine-grained seam. When cooling, the slag lifts itself and the seam remains clean without additional mechanical impact.

Additional

Package type

Box	Vacuum tube

Weight: 1 kg, 1.5 kg, 1.9 kg, 2.5 kg, 5 kg

Diameter: 2 mm, 2.5mm, 3 mm, 4 mm, 5 mm, 6 mm

Welding electrodes PEOK-46.00 FLAGMAN

Description of the electrodes

• They have high adhesion. If the storage conditions are met, they do not require calcination before welding.
• In case of humidification, calcination at a temperature of 90-100 °For 30 minutes (for ø 2.5 and 3.0 mm) and 120-130°C for 1 hour (for ø 4.0 and 5.0 mm), the surfacing coefficient of the PEOC electrodes is 46.00, the FLAGMAN is 8.5-9.2 g/A*hour.
• The consumption of electrodes per 1 kg of deposited metal at PEOK is 46.00, the FLAGMAN is 1.69 kg.
• For better primary ignition, an ionizing layer is applied to the ends of the PEOK-46.00 FLAGMAN electrodes.

Scope of application

The PEOK-46.00 FLAGMAN electrodes are designed for welding any structures made of carbon and low-alloy steel. Welding can be carried out even by a novice welder on devices of the budget segment. Electrodes are indispensable for welding in "fields" with low current strength. The surface may be wet, with traces of rust and other contaminants. The PEOK-46.00 FLAGMAN electrode melts quietly during welding, creates almost no splashes, and forms a fine-scaled seam. When cooling, the slag is easily separated and the seam remains clean. It has high adhesion, which allows welding in hard-to-reach places, bending the electrode to any angle.

Additional

Package type

Box	Vacuum tube

Weight: 1 kg, 1.5 kg, 1.9 kg, 5 kg

Diameter: 2.5mm, 3 mm, 4 mm, 5 mm, 6 mm

Comparative characteristics

So, based on these characteristics, you can choose the appropriate electrodes.

Remember the simple rule: there are no better electrodes at all — there are better electrodes for your specific task. Focus on the type of metal, the welding conditions (for example, the need to weld a vertical seam) and the desired quality of the result. Compare offers based on these parameters, and your work will be effective and the result will be reliable.